|Material:||200 300 400||Surface:||Bright|
|Coil Inner Diameter:||250-1000mm||Standard:||JIS G. EN. ASTM. DIN. GB Etc|
|Packing:||Coil Or Special Packing With Plate||Status:||Full Hard|
ss binding wire,
stainless steel spring wire
Stainless steel spring wire Austenite spring wrie
302 is a variations of the 18% chromium / 8% nickel austenitic alloy, which is the most familiar and the most frequently used in the stainless steel family. Alloy 302 is a slightly higher carbon version of 304, often found in strip and wire forms. It is a tough, ductile grade that demonstrates comparable corrosion resistance, is non-magnetic, and is not hardenable by heat treatment. Alloy 302 is usually used in its annealed condition and has a high ease of fabrication and formability.
7X24-hour Telephone Consulting Service is available.
Reply and solution will be provided in 8 hours upon customer’s service request.
After-sales Support is available on a 7X24-hour basis, leaving no worries for customers.
Quality inspection from raw material to production, and delivery.
Professional quality control person, to avoid the unqualified products flowing to customer.
Strict inspection to Raw material, production, and delivery.
Full series of equipment in quality laboratory.
|302||max: 0.15||max:2.0||max: 0.75||max: 0.045||max: 0.03||min: 17.0 max: 19.0||min: 8.0 max: 10.0||max: 0.10|
|Grade||Tensile Strength ksi (min)||Yield Strength 0.2% ksi (min)||Elongation %||Hardness (Rockwell B) MAX|
(BTU/h ft. °F)
(in x 10-6)
(psi x 106
°F x 10-6
|at 68°F: 0.285||9.4 at 212°F||72.0 at 70°F||28||9.6 at 32 – 212°F||0.1200 at 32°F to 212°F||2500 to 2590|
|12.4 at 932 °F||10.2 at 32 – 1000°F|
|10.4 at 32 – 1500°F|
1, Provides useful resistance to corrosion on a wide range of moderately oxidizing to moderately reducing environments
2, The 18 -19% of chromium which this alloy contains provides resistance to oxidizing environments such as dilute nitric acid.
3, Resistant to moderately aggressive organic acids such as acetic, and reducing acids such as phosphoric.
4,’ The 9-11% of nickel contained in this alloy provides resistance to moderately reducing environments.
Uniform heating to 2100oF will allow this allow to be forged, upset and headed successfully
Do not work below 1700oF
Will dramatically increase the hardness of this material; however, it is quite ductile and may readily be drawn, spun and upset
Causes alloy 302 to become magnetic
Post-fabrication annealing is necessary to retain maximum corrosion resistance and a non-magnetic condition